| No. | Product | CAS No. | Main Parameter | Main Application | Certification or Registration | Factory |
| 1 | Biaxially oriented polyethylene: BOPE-1 BOPE-2 |
9002-88-4 | BOPE-1: Melt flow rate 2.5g/10min Density 0.922g/cm3 Film TD tensile strength > 70MPa BOPE-2: Melt flow rate 2.0g/10min Density 0.924g/cm3 Film TD tensile strength > 70MPa |
BOPE(Biaxially oriented polyethylene) film, food package, agricultural greenhouse, weight package | BRICI | |
| 2 | Environmentally friendly polyolefin heat shrinkable film: DFDA-6010 | 9002-88-4 | Melt flow rate 0.95g/10min Tensile yield strength 10MPa Haze 14% Tensile break strength 30MPa |
POF film, high-grade packaging film, all kinds of composite film base film | Tianjin | |
| 3 | Ethylene/ hexane copolymer: HD6007XA |
9002-88-4 | Melt flow rate 0.6g/10min Density 0.962g/cm3 Tensile stress at yield 26MPa Nominal tensile strain at break 700% Charpy impact strength 10kJ/m2 Environmental stress-cracking ≥ 20h |
Small hollow milk bottle with special grade and less odor | Tianjin | |
| 4 | High melt strength polypropylene: E02ES |
9003-07-0 | Melt flow rate 2.0g/10min Charpy impact strength 7.4kJ/m2 Flexural modulus 1150MPa Melt strength 0.231N |
Extrusion sheet, foamed board, waterproofing materials | Zhenhai | |
| 5 | Low density polyethylene(LDPE): LF5000 |
9002-88-4 | Melt flow rate 40g/10min Density 0.919g/cm3 |
Microfiber, microfiber PU leather | Shanghai | |
| 6 | Very low density polyethylene(LLDPE): TJVL-1210 |
9002-88-4 | Melt flow rate 1.0g/10min Tensile yield strength 8.9MPa Haze 12% Dart impact strength 226g Density 0.910g/cm3 Tensile break strength 30MPa |
Polypropylene modifier, wrap film viscous layer, low temperature frozen packaging, low temperature cling film | Tianjin | |
| 7 | Low density polyethylene super fibre material: 1I60A |
9002-88-4 | Melt flow rate 60g/10min | Manufacturing plastic flowers, paintings on appliances, melt adhesive and super fibre clothes |
Yanshan | |
| 8 | No-plasticize-agent no-woven cloth special resin: PPH-Y35X PPH-Y55 |
9003-07-0 | PPH-Y35X: Melt flow rate 36g/10min Molecular weight distribution 3.2 PPH-Y55: Melt flow rate 64g/10min Molecular weight distribution 5.2 |
Disposable surgical gown, diaper, sanitary napkin, and other medical materials | ROHS | Luoyang |
| 9 | Polybutylene terephthalate (PBT Resin) |
26062-94-2 | Intrinsic viscosity 0.7～1.4dl/g | Plastic, fiber, optical cable, film, etc. | ROHS FDA |
Yizheng |
| 10 | Polypropylene/ Antibacterial impact copolymer: PPBMN09KJ(QP73NKJ) PPBM10KJ(QPK10) |
9003-07-0 | PPBMN09KJ: Melt flow rate 9g/10min Tensile yield strength 28MPa Flexural modulus 1300MPa Charpy impact strength 8.0kJ/m2 (23℃), 3.5kJ/m2 (-20℃) PPBM10KJ: Melt flow rate 10g/10min Tensile yield strength 20MPa Flexural modulus 920MPa Charpy impact strength 56.0kJ/m2 (23℃), 7.85kJ/m2 (-20℃) Antibacterial rate >99% Fungal growth level 1 Grade |
Injection molding, household electronic devices, automotive upholstery |
Qilu | |
| 11 | Polypropylene/High impact transparent copolymers: PPBMT20(QCT20N) PPBMT08(QCT08N) |
9003-07-0 | PPBMT20: Melt flow rate 20g/10min Tensile yield strength 24MPa Haze 12%～14% Charpy impact strength 8.0kJ/m2 (23℃), 1.1kJ/m2 (-20℃) PPBMT08: Melt flow rate 10g/10min Tensile yield strength 23MPa Haze 12%～14% Charpy impact strength 31.0kJ/m2 (23℃), 1.1kJ/m2 (-20℃) |
Frozen food packaging, high gloss translucent furniture, automotive upholstery, half flexible container and lid, medical syringes | Qilu | |
| 12 | Low XS Clarified polypropylene (G Resin): PPR-MT12-S PPR-MT18-S |
9003-07-0 | PPR-MT12-S: Melt flow rate 10.7g/10min Flexural modulus 1300MPa Haze 8.1% PPR-MT18-S： Melt flow rate 19.8g/10min Charpy impact strength 2.0kJ/m2 Haze 12.4% |
Milk bottle, food containers, stationery, packaging materials and housewares | PPR-MT12-S: Food Grade(GB), FDA, RoHS, PAHs, REACH PPR-MT18-S: Food Grade(GB), FDA, RoHS, PAHs, REACH, EN71-3, CP65, CHCC, BPA, 17P, 6P |
Maoming |
| 13 | Propylene/Butene random copolymers: M1500B M850B E980BHF F280B |
9003-07-0 | M1500B: Melt flow rate 15g/10min M850B: Melt flow rate 8g/10min E980BHF: Melt flow rate 12g/10min F280B: Melt flow rate 2.8g/10min |
Transparent injection molding, hot filling bottles, BOPP laser film | Shanghai | |
| 14 | Polypropylene/High impact transparent copolymer: PPB-MT25-S |
9003-07-0 | Melt flow rate 24.8g/10min Flexural modulus 868MPa Charpy impact strength 11.1 kJ/m2 Haze 17.5% |
Transparent injection molding transparent products | Food Grade(GB), FDA, RoHS, PAHs, REACH, 17P, Food Grade(EU) | Maoming |
| 15 | High crystallinity polypropylene resin with Low ash： PPH-FA03 |
9003-07-0 | Melt flow rate 3.0g/10min Tensile stress 32MPa Modulus of elasticity in tension 1580MPa Nominal tensile strain at break 360% Isotacticity index 98.4wt% Ash 39 ppm wt |
Lithium battery separator and other electrical membrane | Food Grade(GB), FDA, RoHS, PAHs, REACH, 17P, EU Food Grade | Zhongyuan |